High Strength 7075 T6 Forged Cone Aluminum Forging Parts
7075 aluminum forged cone parts
7075 aluminum alloy is a cold-treated forging alloy with high
strength, far better than mild steel. 7075 is one of the most
powerful alloys commercially available. Common corrosion
resistance, good mechanical properties and anode reaction. The
finer grains make the deep drilling performance better, the tool
wear resistance is enhanced, and the thread rolling is more
distinctive. Zinc is the main alloying element in 7075. Adding
magnesium to alloys containing 3%-7.5% zinc can form MgZn2 with a
significant strengthening effect, making the alloy's heat treatment
effect far better than aluminum-zinc binary alloys. Increasing the
zinc and magnesium content in the alloy will further improve the
tensile strength, but its resistance to stress corrosion and
spalling corrosion will decrease. After heat treatment, it can
reach very high strength characteristics. 7075 materials are
generally added with a small amount of copper, chromium and other
alloys. Among the series, 7075-T651 aluminum alloy is particularly
top-grade, and it is known as the best product among aluminum
alloys, with high strength and far better than any mild steel. This
alloy also has good mechanical properties and anodic reaction.
Representative uses include aerospace, mold processing, mechanical
equipment, tooling and fixtures, especially for the manufacture of
aircraft structures and other high-stress structures that require
high strength and strong corrosion resistance.
Physical properties
Tensile strength: 524Mpa
0.2% yield strength: 455Mpa
Elastic modulus E: 71GPa
Hardness: 150HB
Density: 2.81g/cm^3
Features
1. High-strength heat-treatable alloy.
2. Good mechanical properties.
3. Good usability.
4. Easy to process and good wear resistance.
5. Good corrosion resistance and oxidation resistance.
Specifications On 7075 T6 Aluminum Forged Cone
Diameter Range: 55mm Through 338mm
Wall Thickness Range: 35mm Through 89mm
Application: Missle Heads
Shape: Cone